| 详细介绍： 液晶聚合物 LCP 美国杜邦 7130L BK010 玻璃纤维30％填充增强 添加润滑剂 抗撞击性好 耐热性高
LCP - 7130L 物性表
①原料描述部分
|
暂无此原料描述部分┄
|
②原料技术数据
|
性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
物理性能
|
比重
|
黑色
|
ASTM D-792
|
1.62
|
---
|
泰伯摩擦
|
---
|
ASTM D-1044
|
63
|
mg
|
模缩率
|
流向1.6mm
|
ASTM D-955
|
-0.1
|
%
|
模缩率
|
流向3.2mm
|
ASTM D-955
|
0
|
%
|
模缩率
|
横向1.6mm
|
ASTM D-955
|
0.9
|
%
|
机械性能
|
模缩率
|
横向3.2mm
|
ASTM D-955
|
0.8
|
%
|
洛氏硬度
|
Scale M
|
ASTM D-785
|
63
|
---
|
冲击下机械性能
|
---
|
UL 746B
|
210
|
ºC
|
拉伸强度
|
23℃,1.6mm
|
ASTM D-638
|
173
|
MPa
|
拉伸强度
|
23℃,3.2mm
|
ASTM D-638
|
150
|
MPa
|
断裂伸长率
|
23℃,1.6mm
|
ASTM D-638
|
1.6
|
%
|
断裂伸长率
|
23℃,3.2mm
|
ASTM D-638
|
1.7
|
%
|
拉伸模量
|
23℃,1.6mm
|
ASTM D-638
|
19306
|
MPa
|
拉伸模量
|
23℃,3.2mm
|
ASTM D-638
|
18000
|
MPa
|
弯曲模量
|
23℃,0.8mm
|
ASTM D-790
|
18000
|
MPa
|
弯曲模量
|
23℃,1.6mm
|
ASTM D-790
|
14000
|
MPa
|
弯曲模量
|
23℃,3.2mm
|
ASTM D-790
|
13100
|
MPa
|
无缺口冲击强度
|
23℃,1.6mm
|
ASTM D-4812
|
840
|
j/m
|
无缺口冲击强度
|
23℃,3.2mm
|
ASTM D-4812
|
555,20%NB
|
j/m
|
弯曲强度
|
23℃,0.8mm
|
ASTM D-790
|
215
|
MPa
|
弯曲强度
|
23℃,1.6mm
|
ASTM D-790
|
192
|
MPa
|
弯曲强度
|
23℃,3.2mm
|
ASTM D-790
|
183
|
MPa
|
压缩强度
|
3.2mm
|
ASTM D-695
|
89
|
MPa
|
弯曲疲劳
|
3.2mm，69MPa
|
ASTM D-671
|
2667
|
cycle
|
IZOD冲击强度
|
23℃,0.8mm
|
ASTM D-256
|
400,40%NB
|
j/m
|
IZOD冲击强度
|
23℃,1.6mm
|
ASTM D-256
|
170
|
j/m
|
IZOD冲击强度
|
23℃,3.2mm
|
ASTM D-256
|
225
|
j/m
|
电气性能
|
介电强度
|
1.6mm逐步
|
ASTM D-149
|
31
|
KV/mm
|
介电强度
|
23℃,1.6mm短时间
|
ASTM D-149
|
35
|
KV/mm
|
介电强度
|
23℃,3.2mm短时间
|
ASTM D-149
|
＞28
|
KV/mm
|
表面电阻率
|
---
|
ASTM D-257
|
1×1015
|
Ω
|
体积电阻率
|
---
|
ASTM D-257
|
1×1016
|
Ω.cm
|
损耗因素
|
23℃,3.2mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
损耗因素
|
23℃,0.8mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
损耗因素
|
23℃,1.6mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
损耗因素
|
23℃,0.8mm,1×103Hz
|
ASTM D-150
|
0.013
|
---
|
损耗因素
|
23℃,3.2mm,1×103Hz
|
ASTM D-150
|
0.013
|
---
|
损耗因素
|
23℃,0.8mm,1×106Hz
|
ASTM D-150
|
0.029
|
---
|
损耗因素
|
23℃,3.2mm,1×106Hz
|
ASTM D-150
|
0.029
|
---
|
介电常数
|
23℃,0.8mm,1×103Hz
|
ASTM D-150
|
3.9
|
---
|
介电常数
|
23℃,3.2mm,1×103Hz
|
ASTM D-150
|
4.3
|
---
|
介电sup>6Hz
|
ASTM D-150
|
3.5
|
---
|
|
介电常数
|
23℃,3.2mm,1×106Hz
|
ASTM D-150
|
3.8
|
---
|
介电常数
|
23℃,0.8mm,1×109Hz
|
ASTM D-2520B
|
4.4
|
---
|
介电常数
|
23℃,3.2mm,1×109Hz
|
ASTM D-2520B
|
4.3
|
---
|
加工性能
|
熔解温度范围
|
℃
|
---
|
363～371
|
---
|
模具温度范围
|
℃
|
---
|
30～95
|
---
|
干燥时间（除湿干燥剂）
|
---
|
---
|
2
|
h
|
干燥温度
|
---
|
---
|
135
|
℃
|
加工时水气含量
|
---
|
---
|
＜0.01
|
%
|
热 性 能
|
相关温度指数
|
---
|
UL 746B
|
240
|
ºC
|
熔点
|
---
|
ASTM D-3418
|
352
|
ºC
|
导热性
|
---
|
ASTM C-177
|
0.32
|
W/m k
|
热变形温度
|
---
|
ASTM D-648
|
289
|
ºC
|
玻璃转变温度
|
---
|
ASTM D-3418
|
120
|
ºC
|
外推最终融温
|
---
|
ASTM D-3418
|
360
|
ºC
|
其它性能
|
厚度测试
|
---
|
UL 94
|
0.75
|
mm
|
限制氧气指数
|
3.2mm
|
ASTM D-2863
|
39
|
%
|
厚度比率
|
---
|
UL 94
|
V-0
|
---
|
|
放大图片